Brandon Bocklund

There are currently some systematic issues with ionic solids that I'm working on separately. I tried to flip through some of the phase diagram collection and pick out systems that...

The MatCalc Al database in the workshop material has been fixed now https://github.com/materialsgenomefoundation/2023-workshop-material/tree/03be5e6300feffc9350ad5094b7e9485b26f1c42/pycalphad/databases #541 improves the error message so it's easier to track which phases cause the issue. The phase...

As this is a database issue, I think it's sufficiently resolved to close.

From https://github.com/PhasesResearchLab/ESPEI `python -m readme_renderer -f rst README.rst` (`.txt` extension added for the upload to GitHub to work) Gives output: ``` :37: (WARNING/2) Cannot scale image! Could not get size...

Sorry, there's lots of whitespace changes as my editor trims whitespace on save

1. I haven't wired that up. There would be a gotcha that system mass likely wouldn't work because we currently require system moles = 1. My experience with the linear...

Thanks for your question and sharing the output. 1. Which version of PyCalphad and Scheil are you using? From this output, it looks like you might be using a slightly...

Okay. I asked about versions because Scheil 0.3.0 shouldn't produce `eq_phases [...]` output, so it looked old to me. From a high-level view, it's not surprising that adding a new...

@wahab2604 sorry we lost track of this. I'm not sure if it's a GitHub thing, but attachments don't seem to persist. If you can provide those again, those would be...

@Zhyrek can you still reproduce this? I wasn't able to trigger the behavior even if I put `/-` into a phase and called into `pr.obj` with reasonable inputs. I'm testing...