Philip-Go

Hello Marc and Hakon, thanks for your quick reply! The following link gives you an .h5oina file of a 75 x75 EBSD mapping of an Aluminum sample: [https://faubox.rrze.uni-erlangen.de/getlink/fiTbeDDgQ8ZfSz7ocD87vh/Al_SLBM%2010kV_8x8_small.h5oina](url) The Kikuchi-Pattern...

That might be off topic regarding EMsoft, but the resulting IPf map looks well indexed. Does PyEBSDIndex achieve such a high indexation rate by hough indexing alone or was the...

Hi Marc, the detector geometry values we measured and obtained from Oxford are (as stated above): tilt: 5°-6°, but could be 6.5°, I haven't obtained it more accurately, but this...

Hello Marc, thank you very much for looking into the file. I went offline for the last 2 days, but thank you for waiting for my reply. I performed a...

> Hi Philip, > > that is reasonably good agreement between the two DI results; a change in pattern center will always give a light rotational difference between the two...

Hello Marc, thank you very much for sharing the conversion script! It works smoothly and can nicely be integrated into the execution script. I have tested it over the weekend...

I found a solution to the y-PC Calculation for Oxford EBSD Diffration Patterns. Maybe it is still of interest. I have been struggling with Pattern Centers from Oxford/AZtec troughout the...